Ni220M1 Glass Mold Cladding Powder from China Suppliers - Innovative Factory Solutions for Enhanced Efficiency
Performance characteristics
Precision Process
Consistent Reliability
Utilizing high-temperature smelting at 1650-1700°C and 99.999% pure argon gas atomization, the process eliminates compositional segregation. The powder’s 45-150μm (100-325 mesh) particle size distribution ensures high sphericity and flowability (apparent density: 4.2g/cm³, flow rate: 14-16s/50g), providing stable powder feeding for plasma transferred arc welding (PTAW) and laser cladding processes.
Optimal Balance
Long-Term Durability
The innovative composition (C 0.03%, Cr 4.9%, B 1.0%, Si 3.0%) maintains low hardness (HRC 22-24) and exceptional ductility while forming erosion-resistant phases against molten glass. Post-polishing, the cladding layer achieves defect-free surfaces (zero pinholes/porosity). Enhanced metallurgical bonding through Fe-Mn element optimization triples mold service life.
Efficient Compatibility
Green Manufacturing
Adaptable to both high-speed large-area PTAW deposition and precision laser cladding repairs, the low heat input minimizes substrate deformation. With material utilization exceeding 95%, it enables energy-efficient production of durable mold working surfaces, significantly reducing maintenance costs.
Choosing Ni220M1 means securing dual guarantees of high-quality output and sustainable production, injecting innovative momentum into the glass manufacturing industry!
Frequently Asked Questions
What is the particle size distribution of Ni220M1 powder?
What is the hardness level and chemical composition of this cladding material?
Which welding and cladding processes are compatible with Ni220M1?
How does this powder improve the service life of glass molds?
What is the material utilization rate of Ni220M1?
What to know about this product?